·   MFE 707N combines the novolac backbone typical of MFE 770 and MFE 780 with a brominated epoxy resin backbone, so MFE 707N own excellent corrosion resistance and high temperature resistance properties with good toughness and reduced flammability.

·  Laminates made with MFE 707N resin meet ASTM E-84 Flame Spread “Class 2” rating (less than 75). 3% of antimony oxide (Sb₂O₃), Class 1 ratings can be achieved (1).

·   MFE 707N owns best performance against wet or dry chlorine gas, chlorine dioxide, bleach, and hot, wet flue gas environments within MFE series vinyl ester resins. Corrosion resistance quit similar or equals to MFE 770 and MFE 780.

 · When fire retardance, heat resistance and / or corrosion resistance are required at the same time.

·  Widely used to produce FRP ductwork, stacks and stack liner applications, equipment specified to handle mixtures of air and hot gases or potentially flammable and corrosive liquids, and floorings compounds where a high degree of heat and / or fire resistance is needed.

·  FRP fabrication processes such as filament winding, hand lay-up, spray-up, pultrusion and infusion (RTM). 

(1) The fire retardancy and flame spread data were obtained from controlled and/or small scale bench tests and the results apply specifically to the specimens tested, in the manner tested. They are not necessarily predictive of product performance in a real fire situation. MFE resins are organic materials and the fabricated products constructed from them will burn under the right conditions of heat and oxygen supply. This numerical flame spread rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(2)Typical property values only, not to be construed as specifications
(3) Unopened drum with no additives, promoters, accelerators, etc. added. Shelf life specified from date of manufacture

(2) Typical property values only, not to be construed as specifications.
(4) Cure schedule: 24 hours at room temperature; 2 hours at 120°C (250°F)
(5) Maximum stress: 1.8 MPa (264 psi)

This resin contains ingredients which could be harmful if mishandled. Contact with skin and eyes should be avoided and necessary protective equipment and clothing should be worn.

The specification is 2010 edition and may change with the technological improvement.

Huachang Polymer Co., Ltd. of ECUST maintains Material Safety Data Sheets on all of its products. Material Safety Data Sheets contain health and safety information for your development of appropriate product handling procedures to protect your employees and customers.

Our Material Safety Data Sheets should be read and understood by all of your supervisory personnel and employees before using Huachang’s products in your facilities.

Non-returnable steel drums, net weight is 200kg per drum

Drums - Store at temperatures below 25℃. Storage life decreases with increasing storage temperature. Avoid exposure to heat sources such as direct sunlight or steam pipes. To avoid contamination of product with water, do not store outdoors. Keep sealed to prevent moisture pick-up and monomer loss. Rotate stock. For more information, please contact us at huachang@hchp.com.cn

Naphthenate-6% (CoNap6%), Diethylaniline (DEA), and 2,4-Pentanedione
(2,4-P).Use of other MEKP or other additives may result in different gel time results.
(6) Use of cobalt octoat
(7) Phr=parts per hundred resin molding compound
e, especially in combination with 2,4-P can result in 20-30% slower gel times.